What problems may be encountered when welding sintered mesh?

Sintered mesh products will be welded during the production process, so what problems may be encountered during the welding work? Below, I will introduce some problems that you may encounter when welding this product.

First of all, when the sintered wire mesh product is welded during production, it may be hardened due to the high temperature at the weld, especially for stainless steel products. Due to the hardenability of stainless steel, it will cause welding during welding. The heat affects the hardening phenomenon, and at the same time, it will also cause the crack phenomenon.

In addition, when the sintered mesh wire welded happens during production, it may also encounter hysteresis cracks, that is, after the product has been welded, cracks appear after a few days, and its position will be in the same position as the weld metal. right angle phenomenon.

The above content is some problems that may be encountered when welding sintered mesh products during production. I hope that everyone will pay more attention to the above problems when welding this product in the future. In addition, if you have any questions, please feel free to consult.